Characterizations of Ce 3+-doped CaB 2O 4 crystalline scintillator

Yutaka Fujimoto, Takayuki Yanagida, Noriaki Kawaguchi, Shunsuke Kurosawa, Kentaro Fukuda, Daisuke Totsuka, Kenichi Watanabe, Atsushi Yamazaki, Yuui Yokota, Akira Yoshikawa

研究成果: Article査読

15 被引用数 (Scopus)

抄録

Single crystals of undoped and 0.5% Ce 3+-doped calcium metaborate CaB 2O 4 have been grown successfully by micropulling down (μ-PD) technique. The material can find its application in the neutron detection. After the single-phase of CaB 2O 4 was confirmed using X-ray diffraction analysis, optical and scintillation characteristics were investigated. In the transmittance spectra, Ce 3+-doped crystals showed absorption bands around 270 and 320 nm which are ascribed to the transition from 4f ground state to 5d excited state of Ce 3+. Under the 241Am 5.5 MeV α-ray excitation, strong emission peak at 370 nm because of the Ce 3+ 5d-4f transition was observed for Ce 3+-doped crystal, while the undoped crystal showed broad intrinsic emission band around 300-400 nm which is caused by the lattice defects in the host crystal. The absolute light yield was calculated to be about 2200 photons per neutron under 252Cf neutron irradiation.

本文言語English
ページ(範囲)142-146
ページ数5
ジャーナルCrystal Growth and Design
12
1
DOI
出版ステータスPublished - 2012 1 1

ASJC Scopus subject areas

  • 化学 (全般)
  • 材料科学(全般)
  • 凝縮系物理学

フィンガープリント

「Characterizations of Ce <sup>3+</sup>-doped CaB <sub>2</sub>O <sub>4</sub> crystalline scintillator」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル