Characterization of ultrafine SiC-Si3N4 composite powder after heat-treatment in Ar + N2

Xingguo Li, Akihiko Chiba, Yoshinori Nakata, Hideaki Nagai, Masaaki Suzuki

研究成果: Article査読

16 被引用数 (Scopus)

抄録

Ultrafine SiC-Si3N4 composite powder synthesized by laser-induced gas-phase reaction was heat-treated at a temperature range of 295-1773 K in a mixture gas flow of Ar + N2. The changes in crystalline structure, shape, particle size, crystalline size, chemical composition, specific surface area and defect state were investigated by X-ray diffraction (XRD), transition electron microscope, chemical analysis, specific surface area analysis and electron spin resonance. No significant changes in the structure are observed after the heat treatment below 1673 K in Ar + N2, similar to the result of the heat-treatment in Ar. At or above 1673 K, the characteristic changes occur, but these depend on the heating atmosphere. The precipitation of metallic silicon, which is observed in the heat-treatment in Ar, is suppressed by introducing only 5% N2 to the atmosphere. The composite powder with a desired composition of SiC and Si3N4 can be obtained by adjustment of the nitrogen partial pressure.

本文言語English
ページ(範囲)95-101
ページ数7
ジャーナルMaterials Science and Engineering A
219
1-2
DOI
出版ステータスPublished - 1996 11月 30
外部発表はい

ASJC Scopus subject areas

  • 材料科学(全般)
  • 凝縮系物理学
  • 材料力学
  • 機械工学

フィンガープリント

「Characterization of ultrafine SiC-Si3N4 composite powder after heat-treatment in Ar + N2」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル