Shenmin Zhu, Haoshen Zhou, Mitsuhiro Hibino, Itaru Honma, Masaki Ichihara

研究成果: Article査読

19 被引用数 (Scopus)

抄録

The dependence of pore size of carbon-coated ordered channels of mesoporous SBA-15 on temperature is reported for the first time from characterization of as-synthesized SBA-15 after graphitization under nitrogen at relatively high temperatures. The pore sizes of the obtained products changed, respectively, from 6.8 to 7.9 and 7.3 nm, corresponding to graphitization temperature of 800-600 and 500°C. The formation of carbon from the template acts as a framework support that reduces the shrinkage of the pores when as-synthesized SBA-15 is heat treated at high temperature under nitrogen, resulting in materials with larger pores than in calcined SBA-15, Thus, adjusting the heat-treating temperature can control the pore size of the resultant carbon-coated samples. This is likely to play an important role in its potential use as adsorbents or in electrochemistry.

本文言語English
ページ(範囲)202-206
ページ数5
ジャーナルMaterials Chemistry and Physics
88
1
DOI
出版ステータスPublished - 2004 11月 15
外部発表はい

ASJC Scopus subject areas

  • 材料科学(全般)
  • 凝縮系物理学

フィンガープリント

「Characterization of the dependence on temperature of the formation of carbon film on the internal surfaces of SBA-15 silica」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル