Microstructure and local deformation in 316NG weld heat-affected zones were measured by electron-back scattering diffraction and hardness measurements. With increasing the distance from the fusion line, kernel average misorientation decreases and the fraction of Σ3 boundaries increases. Stress corrosion cracking growth rates in high temperature water were measured at different locations in the heat-affected zones that correspond to different levels of strain-hardening represented by kernel average misorientation and hardness distribution. Intergranular cracking along random boundaries as well as extensive intergranular crack branching is observed in the heat-affected zone near the weld fusion line.