Change in tensile and fatigue properties of biomedical Ti-29Nb-13Ta-4.6Zr alloy fabricated by various processings

Toshikazu Akahori, Mitsuo Niinomi, Masaaki Nakai, Michiharu Ogawa

研究成果: Conference contribution

1 被引用数 (Scopus)

抄録

The tensile and plain fatigue properties of the β-type titanium alloy, Ti-29Nb-13Ta-4.6Zr alloy (TNTZ), which was subjected to various thermomechanical treatments, and cast TNTZ were investigated in order to judge its potential for biomedical and dental applications. The tensile strengths of TNTZ aged after solution treatment and that aged after cold rolling decrease with an increase in the aging temperature; however, their elongation exhibits an opposite trend. TNTZ composed of the ω phase or the ω and α phases in the β phase exhibits a tensile strength of about 1000 MPa or more. The tensile properties of the cast TNTZ with and without a surface reaction layer is are not significantly different, and are almost identcal to those of as-solutionized TNTZ. The plain fatigue strengths of TNTZ aged after solution treatment and those of TNTZ aged after cold rolling increase with the aging temperature. In particular, TNTZ aged at 723 K after cold rolling exhibits the highest fatigue strength in both the low- and high-cycle fatigue life regions. Further, the plain fatigue limit, which is about 770 MPa, is nearly equal to that of hot-rolled Ti-6Al-4V ELI alloy subjected to aging after solution treatment; Ti-6Al-4V ELI alloy is a representative α+β-type titanium alloy for biomedical applications. The plain fatigue strength of cast TNTZ with a surface reaction layer is considerably less than that of the as-cold-rolled and as-solutionized TNTZ. Consequently, in the low-fatigue life region, the fatigue crack easily occurs at the surface reaction layer, which is brittle, and in the high-fatigue life region, the fatigue crack occurs at the sites of casting defects (shrinkage). The fatigue limits range from 180 MPa to 200 MPa.

本文言語English
ホスト出版物のタイトルSelected, peer reviewed papers from The Sixth Pacific Rim International Conference on Advanced Materials and Processing, PRICM 6
出版社Trans Tech Publications Ltd
ページ1505-1508
ページ数4
PART 2
ISBN(印刷版)0878494626, 9780878494620
DOI
出版ステータスPublished - 2007 1 1
外部発表はい
イベント6th Pacific Rim International Conference on Advanced Materials and Processing, PRICM 6 - Jeju, Korea, Republic of
継続期間: 2007 11 52007 11 9

出版物シリーズ

名前Materials Science Forum
番号PART 2
561-565
ISSN(印刷版)0255-5476
ISSN(電子版)1662-9752

Other

Other6th Pacific Rim International Conference on Advanced Materials and Processing, PRICM 6
CountryKorea, Republic of
CityJeju
Period07/11/507/11/9

ASJC Scopus subject areas

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering

フィンガープリント 「Change in tensile and fatigue properties of biomedical Ti-29Nb-13Ta-4.6Zr alloy fabricated by various processings」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル