Case study of a 20 T-φ400 mm room temperature bore superconducting outsert for a 45 T hybrid magnet

K. Watanabe, S. Awaji, G. Nishijima, T. Hamajima, T. Kiyoshi, H. Kumakura, S. Hanai, M. Ono

研究成果: Article査読

15 被引用数 (Scopus)


The High Field Laboratory for Superconducting Materials (HFLSM) and the Tsukuba Magnet Laboratory (TML) conducted in collaboration a case study on development of a 50 T-class hybrid magnet. To construct a high magnetic field magnet with compact and energy-saving design as well as with easy operation and maintenance, one has to develop high-strength Nb3Sn strand cables, with maximized superconducting characteristics and which can withstand a large electromagnetic force over 500 MPa. For this purpose, the HFLSM has proposed and investigated the effect of repeated bending treatment (prebending) on Nb 3Sn strands internally reinforced with CuNb stabilizer leading to significant enhancement of the critical current density. In this report we present our results on application of the prebending effect to the development of high-strength strand cables. The designed prebent-strand cables are composed of three CuNb/Nb3Sn strands (3 × φ = 1.73 mm) and four stainless steel strands (4 × φ = 1.73 mm). High-strength CuNb/Nb 3Sn strand cables have shown a stress limit of 552 MPa at 0.4% strain, and a critical current of Ic = 1000 A at 18.5 T and 2.0 K. For such high-strength strand cables, a 20 T superconducting magnet with a room temperature bore (φ = 400 mm) consisting of five layers made of CuNb/Nb 3 Sn and two layers of NbTi was designed. The coil parameters are: inner diameter φ = 440 mm, outer diameter φ = 1332 mm, coil height 1321 mm, inductance 350 H and magnetic stored energy 144 MJ at 908 A of the operation current. Winding of the coil was experimentally successfully simulated using dummy 3 + 4 strands cable composed of three Cu strands and 4 stainless steel strands with a similar design to the 3 + 4 strands superconducting cable presented above. The 20 T superconducting coil will be used as a 20 T outsert for a 25 T water-cooled resistive insert to obtain a 45 T hybrid magnet.

ジャーナルIEEE Transactions on Applied Superconductivity
出版ステータスPublished - 2008 6月

ASJC Scopus subject areas

  • 電子材料、光学材料、および磁性材料
  • 凝縮系物理学
  • 電子工学および電気工学


「Case study of a 20 T-φ400 mm room temperature bore superconducting outsert for a 45 T hybrid magnet」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。