The kinetics of vapor phase dephosphorization from tri-calcium phosphate (TCP) by carbothermic reduction was studied with and without the presence of Fe3O4. Microwave heating was utilized to obtain large variations in the heating rate (HR). In the reduction of TCP alone, the phosphorous removal fraction (RF; equal to ∆P2O5/P2O5 0, where ∆P2O5 is the weight change and P2O5 0 is the P2O5 weight before heating) decreased as the HR increased. In other words, a shorter residence time at a high temperature resulted in a smaller reduction fraction of TCP. An apparently third-order reaction was postulated to account for the kinetics using a fitting simulation based on the additive law of the reaction progress. On the other hand, the phosphorous removal (dephosphorization) rate (RR; equal to ∆P2O3/tMW, where tMW is the microwave heating time period) increased as the HR increased above 1200 °C. The reduction ratio of Fe3O4 above 1100 °C is higher than 97 pct regardless of the heating rate. The reduction of TCP in the presence of Fe3O4 showed that RF increased slightly with increasing HR despite a shorter residence time at a high temperature. The RR also increased with the HR even though RF decreased to half of the values observed in the cases without Fe3O4 for temperatures above 1200 °C. The practicality and optimal operation conditions of phosphorus vapor removal were discussed.
|ジャーナル||Metallurgical and Materials Transactions B: Process Metallurgy and Materials Processing Science|
|出版ステータス||Published - 2018 6月 1|
ASJC Scopus subject areas