Application of a mechanochemical method for recycling waste glass with CO2 solidification

Lihui Liu, Toshiyuki Hashida, Satoshi Teramura

研究成果: Conference contribution

抄録

A mechanochemical method for treatment of powdered (recycled) waste glass and calcium hydroxide is combined with a CO2 solidification process for strength development of solidified products. Our work has potential for reducing CO2 emission, which has been identified as a major cause of global warming. Poorly crystalline pre-pulverized waste glass cullet and calcium hydroxide powder was mixed with ∼70 wt % water and cured at room temperature, prior to CO2 carbonation, to produce a solidified sample. Solidified samples were heated to examine phase transformations. Sample density, Vickers hardness and flexural strength were determined. Effect of grinding time, Ca/Si ratio and water content on the mechanical properties was investigated. The mechanochemical reaction has a strong influence on the hardening process, due to formation of calcium carbonate. TG-DTA results show that the decomposition temperature of the glass/calcium hydroxide mixture is decreased after mechanochemical treatment, indicating enhanced reactivity of the mixture. Vickers hardness is increased after CO2 solidification. Our method is effective for the production of various building materials.

本文言語English
ホスト出版物のタイトルMechanics and Material Engineering for Science and Experiments
編集者Y. Zhou, Y. Ghu, Z. Li, Y. Zhou, Y. Gu, Z. Li
ページ209-213
ページ数5
出版ステータスPublished - 2003 10 17
イベントProceedings of the International Symposium of Young Scholars on Mechanics and Material Engineering for Science and Experiments - Changsha/Zhangjiajie, China
継続期間: 2001 8 112001 8 16

出版物シリーズ

名前Mechanics and Material Engineering for Science and Experiments

Other

OtherProceedings of the International Symposium of Young Scholars on Mechanics and Material Engineering for Science and Experiments
国/地域China
CityChangsha/Zhangjiajie
Period01/8/1101/8/16

ASJC Scopus subject areas

  • 材料科学(全般)
  • 機械工学

フィンガープリント

「Application of a mechanochemical method for recycling waste glass with CO<sub>2</sub> solidification」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル