Anisotropic bonded NdFeB magnets with radial oriented magnetization by 2-step warm compaction process

Siwu Tao, Jianjun Tian, Xin Lu, Xuanhui Qu, Y. Honkura, H. Mitarai, K. Noguchi

研究成果: Article査読

17 被引用数 (Scopus)

抄録

Anisotropic bonded NdFeB magnets obviously have better magnetic properties than those of conventional isotropic bonded NdFeB magnets. The anisotropic bonded magnets can be used to make some magnetic devices with special oriented magnetization, such as radial oriented rings. In order to increase the magnetic properties and prolong the life of the molding die, the anisotropic bonded NdFeB magnets with radial oriented magnetization were prepared by 2-step warm compaction molding, which were called the aligning step and densifying step, respectively. In the aligning step, the magnetic powder particles aligned along the radial direction of the magnetic field (1.0 T) and are compressed under 143 MPa at 393 K. (BH)max and density of the magnets were 146 kJ/m3 and 5.7 g/cm3, respectively. Then the ring compacts were re-compressed under 800 MPa at 420 K in the densifying step. The density increased to 6.2 g/cm3 and magnetic properties were: Br = 0.92 T, Hcj = 1020 kA/m, (BH)max = 168 kJ/m3. SEM micrograph showed that the magnets had excellent microstructure and the magnetic particles were evenly coated by binder. Crown

本文言語English
ページ(範囲)510-514
ページ数5
ジャーナルJournal of Alloys and Compounds
477
1-2
DOI
出版ステータスPublished - 2009 5月 27
外部発表はい

ASJC Scopus subject areas

  • 材料力学
  • 機械工学
  • 金属および合金
  • 材料化学

フィンガープリント

「Anisotropic bonded NdFeB magnets with radial oriented magnetization by 2-step warm compaction process」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル