Adhesion mechanism of cold-sprayed Sn coatings on carbon fiber reinforced plastics

研究成果: Article査読

4 被引用数 (Scopus)

抄録

Metallization of carbon fiber reinforced plastics (CFRPs) has been explored to improve the electrical and thermal conductivities for avoiding thermal degradation and preventing lightning strikes on aircraft. In our recent study, Sn was successfully deposited on a thermosetting-based CFRP using cold spraying. Therefore, this study investigated the adhesion mechanism of the cold-sprayed Sn coatings on the CFRPs prepared at different gas temperatures (473 and 523 K). Herein, pull-off tests were conducted on the specimens deposited at 473 and 523 K, and the obtained results implied that the adhesion strength for the specimen deposited at 523 K was higher. In addition, cross-sectional and superficial observations were carried out after the pull-off test. The obtained results suggest that the chemical reactions between the Sn coating and CFRP substrate hardly occurred during cold spraying. Therefore, mechanical interlocking was considered as the primary mechanism of adhesion. The surface of the CFRP substrate degraded owing to the impacts of stronger particles at higher gas temperatures, representing complex interfacial morphologies that comprise exposed carbon fibers. The resultant rougher surfaces could enhance the mechanical interlocking at the Sn/CFRP interface, thereby improving the adhesion strength.

本文言語English
論文番号151873
ジャーナルApplied Surface Science
579
DOI
出版ステータスPublished - 2022 3月 30

ASJC Scopus subject areas

  • 化学 (全般)
  • 凝縮系物理学
  • 物理学および天文学(全般)
  • 表面および界面
  • 表面、皮膜および薄膜

フィンガープリント

「Adhesion mechanism of cold-sprayed Sn coatings on carbon fiber reinforced plastics」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル