A Study on the Characteristics of Part-Through Crack Growth of Low-Alloy Steel in Corrosive Environment

Hee Don Jeong, Tetsuo Shoji, Hideaki Takahashi, Kenichi Yamaki

研究成果: Article査読

抄録

In order to investigate the characteristics of surface crack growth behavior, the fatigue test and potential measurement using a simulated surface crack specimen for low-alloy steel (STS-42) were achieved in pure water at a temperature of 50°C and an oxygen content of 2 ppm. The potential observed in the surface crack plane showed that the differences depended on the crack depth. With time, the potential around the crack surface showed more noble values than at the deepest tip of crack. This reason could be explained by the difference in oxygen content along the crack plane due to the effect of water flow and crack shape. The mechanism of the generation of the hydrogen-assisted intergranular fracture mode observed at crack surface was also discussed based on an electrochemical aspect.

本文言語English
ページ(範囲)1281-1285
ページ数5
ジャーナルNihon Kikai Gakkai Ronbunshu, A Hen/Transactions of the Japan Society of Mechanical Engineers, Part A
55
514
DOI
出版ステータスPublished - 1989

ASJC Scopus subject areas

  • Materials Science(all)
  • Mechanics of Materials
  • Mechanical Engineering

フィンガープリント 「A Study on the Characteristics of Part-Through Crack Growth of Low-Alloy Steel in Corrosive Environment」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル