T1 - A stable quasicrystal in al-cu-fe system
AU - Tsai, An Pang
AU - Inoue, Akihisa
AU - Masumoto, Tsuyoshi
PY - 1987/9
Y1 - 1987/9
N2 - A thermodynamically stable quasicrystalline single phase with an icosahedral structure was found to be formed at an atomic composition of Al65Cu20Fe15 in a fully annealed state as well as in a conventionally solidified state. The stable quasicrystal consisted of large grains with an average size of 0.2 mm after annealing for 48 h at 1118 K (0.98 Tm).
AB - A thermodynamically stable quasicrystalline single phase with an icosahedral structure was found to be formed at an atomic composition of Al65Cu20Fe15 in a fully annealed state as well as in a conventionally solidified state. The stable quasicrystal consisted of large grains with an average size of 0.2 mm after annealing for 48 h at 1118 K (0.98 Tm).
UR - http://www.scopus.com/inward/record.url?scp=0023416679&partnerID=8YFLogxK
UR - http://www.scopus.com/inward/citedby.url?scp=0023416679&partnerID=8YFLogxK
U2 - 10.1143/JJAP.26.L1505
DO - 10.1143/JJAP.26.L1505
M3 - Article
AN - SCOPUS:0023416679
VL - 26
SP - 1505
EP - 1507
JO - Japanese Journal of Applied Physics, Part 1: Regular Papers & Short Notes
JF - Japanese Journal of Applied Physics, Part 1: Regular Papers & Short Notes
SN - 0021-4922
IS - 9A
ER -