A high field and cryogenic test facility for neutron irradiated superconducting wire

A. Nishimura, H. Miyata, M. Yoshida, M. Iio, K. Suzuki, T. Nakamoto, M. Yamazaki, T. Toyama

研究成果: Conference article査読

2 被引用数 (Scopus)


A 15.5 T superconducting magnet and a variable temperature insert (VTI) system were installed at a radiation control area in Oarai center in Tohoku University to investigate the superconducting properties of activated superconducting materials by fast neutron. The superconductivity was measured at cryogenic temperature and high magnetic field. During these tests, some inconvenient problems were observed and the additional investigation was carried out. The variable temperature insert was designed and assembled to perform the superconducting property tests. without the liquid helium. To remove the heat induced by radiation and joule heating, high purity aluminum rod was used in VTI. The thermal contact was checked by FEM analysis and an additional support was added to confirm the decreasing the stress concentration and the good thermal contact. After the work for improvement, it was affirmed that the test system works well and all troubles were resolved. In this report, the improved technical solution is described and the first data set on the irradiation effect on Nb3Sn wire is presented.

ジャーナルIOP Conference Series: Materials Science and Engineering
出版ステータスPublished - 2017 12月 30
イベント2017 International Cryogenic Materials Conference, ICMC 2017 - Madison, United States
継続期間: 2017 7月 92017 7月 13

ASJC Scopus subject areas

  • 材料科学(全般)
  • 工学(全般)


「A high field and cryogenic test facility for neutron irradiated superconducting wire」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。