(110) grain growth and magnetic properties of thin grain-oriented 3% silicon steel sheets

M. Nakano, K. Ishiyama, K. I. Arai, H. Fukunaga

研究成果: Conference article査読

1 被引用数 (Scopus)

抄録

In this study, the relationship between (110) grain growth and magnetic properties (coercive force Hc and the magnetic induction at 800 A/m B8) at the final-annealing was studied. It was clarified that (110) abnormal grains grew dramatically after FATIME= 0.5 min and the thin sheets with B8 ≅ 1.9 can be obtained at FATIME = 20 min. Further, it was confirmed that an increase of intermediate-annealing temperature (IAT) realizes FATIME = 1 min. to cover the sheets with only (110) grains.

本文言語English
ページ(範囲)BD-11
ジャーナルDigests of the Intermag Conference
出版ステータスPublished - 1999 12 1
外部発表はい
イベントProceedings of the 1999 IEEE International Magnetics Conference 'Digest of Intermag 99' - Kyongju, South Korea
継続期間: 1999 5 181999 5 21

ASJC Scopus subject areas

  • Electrical and Electronic Engineering

フィンガープリント 「(110) grain growth and magnetic properties of thin grain-oriented 3% silicon steel sheets」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル