Wettability between Nd 2Fe 14B and Nd-rich phase in Nd-Fe-B alloy system

Shota Nishio, Ryota Goto, Masashi Matsuura, Nobuki Tezuka, Satoshi Sugimoto

Research output: Contribution to journalArticle

7 Citations (Scopus)

Abstract

The wettability between Nd 2Fe 14B and Nd-rich phases has been investigated through the sessile drop method. The compositions of prepared Nd-rich ingots were Nd 72.0Fe 26.1B 1.9 (ternary) and Nd 72Fe 22.4Cu 3.7B 1.9 (Cu-added). Nd-rich ingots were cut and put on a polished Nd 2Fe 14B plate and heated in a furnace. Contact angles between Nd 2Fe 14B plate and Nd-rich ingots were measured as a parameter of wettability under controlled temperature. For the Cu added sample, both contact angles in all temperature range and temperatures when contact angle starts to change were lower than those for ternary sample. These results indicate Cu substitution yields improvement of wettability. DTA measurements for two Nd-rich ingots reveal that their contact angles starts to change at lower temperature than their melting points It is considered that those phenomena are derived from the existence of Nd 2Fe 14B/Nd-rich interface.

Original languageEnglish
Pages (from-to)1010-1014
Number of pages5
JournalNippon Kinzoku Gakkaishi/Journal of the Japan Institute of Metals
Volume72
Issue number12
DOIs
Publication statusPublished - 2008 Dec 1

Keywords

  • Copper
  • Nd-Fe-B magnet
  • Nd-rich phase
  • Sessile drop method
  • Wettability

ASJC Scopus subject areas

  • Condensed Matter Physics
  • Mechanics of Materials
  • Metals and Alloys
  • Materials Chemistry

Fingerprint Dive into the research topics of 'Wettability between Nd <sub>2</sub>Fe <sub>14</sub>B and Nd-rich phase in Nd-Fe-B alloy system'. Together they form a unique fingerprint.

  • Cite this