Water-gas shift reaction over aluminum promoted Cu/CeO2 nanocatalysts characterized by XRD, BET, TPR and cyclic voltammetry (CV)

Lei Li, Yingying Zhan, Qi Zheng, Yuanhui Zheng, Xingyi Lin, Dalin Li, Junjiang Zhu

Research output: Contribution to journalArticle

65 Citations (Scopus)

Abstract

A series of aluminum promoted Cu/CeO2 nanocatalysts with aluminum content in the range of 0-5wt.% were prepared by co-precipitation method and examined with respect to their catalytic performance for the water-gas shift (WGS) reaction. The catalysts were characterized by XRD, BET, H2-TPR and cyclic voltammetry (CV) techniques. The results indicate that catalytic activity increases with the aluminum content at first, but then decreases with the further increase of aluminum content. Hereinto, Cu/CeO 2 catalyst doped with 1 wt.% of aluminum shows the highest catalytic activity (CO conversion reaches 84.4% at 200 °C) and thermal stability for WGS reaction. Correlation to the results from above characterization, it is found that the variation of catalytic activity is in very agreement with that of the surface area, the area of peak γ (i.e., the reduction of surface copper oxide (crystalline forms) interacted with surface oxygen vacancies on ceria), and the area of peak C2 and A1(Cu0 ↔ Cu2+ in cyclic voltammetry process), respectively. Enough evidence was found for the fact that the metallic copper (Cu0) interacted with surface oxygen vacancies on ceria is the active site for WGS reaction over Cu/CeO2 catalysts.

Original languageEnglish
Pages (from-to)91-97
Number of pages7
JournalCatalysis Letters
Volume118
Issue number1-2
DOIs
Publication statusPublished - 2007 Oct 1

Keywords

  • Active site
  • Aluminum
  • Cu/CeO catalyst
  • Cyclic voltammetry (CV)
  • Water-gas shift

ASJC Scopus subject areas

  • Catalysis
  • Chemistry(all)

Fingerprint Dive into the research topics of 'Water-gas shift reaction over aluminum promoted Cu/CeO<sub>2</sub> nanocatalysts characterized by XRD, BET, TPR and cyclic voltammetry (CV)'. Together they form a unique fingerprint.

  • Cite this