Variation of atomic spacing and thermomechanical properties in Ni-Mn-Ga/alumina film composites

Stefano Besseghini, Tommaso Cavallin, Volodymyr Chernenko, Elena Villa, Victor Lvov, Makoto Ohtsuka

Research output: Contribution to journalArticlepeer-review

20 Citations (Scopus)

Abstract

Ni51.4Mn28.3Ga20.3 thin films deposited on alumina ceramics have been studied by X-ray powder diffraction and dynamic mechanical analysis. Substantial temperature vs. film thickness dependencies of interatomic spacing measured in the direction of the film normal are observed in the range of 25-200 °C and 0.1-5 μm, respectively. The coefficient of thermal expansion (CTE) of the film in the paramagnetic cubic phase has been determined to be equal to (15 ± 1) × 10-6 K-1 for all the films, in agreement with the CTE of bulk material. The thickness dependent shrinkage of the pseudo-cubic lattice along the film normal direction is attributed to the thermally induced tensile stress in the film plane. The thickness dependence of the elastic modulus of submicron films is obtained. It is shown that the internal stresses result in both the thickness dependence of martensitic transformation temperature and the reversible, thermally induced change in shape of the Ni-Mn-Ga/alumina cantilever actuator.

Original languageEnglish
Pages (from-to)1797-1801
Number of pages5
JournalActa Materialia
Volume56
Issue number8
DOIs
Publication statusPublished - 2008 May 1

Keywords

  • Lattice spacing
  • Martensitic transformation
  • Ni-Mn-Ga/alumina film composite
  • Thermomechanical actuation

ASJC Scopus subject areas

  • Electronic, Optical and Magnetic Materials
  • Ceramics and Composites
  • Polymers and Plastics
  • Metals and Alloys

Fingerprint Dive into the research topics of 'Variation of atomic spacing and thermomechanical properties in Ni-Mn-Ga/alumina film composites'. Together they form a unique fingerprint.

Cite this