TRANSVERSE-RUPTURE STRENGTH OF WC-Co CEMENTED CARBIDE COATED WITH TITANIUM NITRIDE BY THE PVD PROCESS.

H. Suzuki, K. Hayashi, H. Matsubara

Research output: Contribution to journalArticle

6 Citations (Scopus)

Abstract

The transverse rupture strength of cemented carbides which were HIP treated and coated by the physical vapor depostion (PVD) process was investigated in relation to thickness (1. 5-5 mu m) of the deposited layer, Co content (5-20%) of the substrate and temperature (923-1273 K) of annealing after PVD at 773 K. Strength in the as-PVD state decreased with increasing thickness and Co content. A decrease was caused by annealing.

Original languageEnglish
Pages (from-to)885-890
Number of pages6
JournalTransactions of the Japan Institute of Metals
Volume25
Issue number12
DOIs
Publication statusPublished - 1984 Jan 1
Externally publishedYes

ASJC Scopus subject areas

  • Engineering(all)

Fingerprint Dive into the research topics of 'TRANSVERSE-RUPTURE STRENGTH OF WC-Co CEMENTED CARBIDE COATED WITH TITANIUM NITRIDE BY THE PVD PROCESS.'. Together they form a unique fingerprint.

  • Cite this