Transmission electron microscopic observation of precipitates in age-hardened die-cast aluminum alloys

Toyohiko J. Konno, Syohei Sasaki, Takumi Hamaoka

Research output: Contribution to journalArticle

1 Citation (Scopus)

Abstract

Squeeze die casting with a composition similar to JIS ADC12 aluminum alloy was aged at 453 K with or without prior solution treatment. Aging following solution treatment, which is termed T6-treatment, increased the hardness of this alloy. Using transmission electron microscopy, we investigated precipitates responsible for the age-hardening. Concentration of solute silicon, copper and magnesium during aging led to the formation of several types of precipitates in the matrix face-centered cubic (fcc) Al-phase. Precipitates exhibiting equiaxed shape and possessing copper-enriched faces at the interface with the Al-phase were observed. We suggest that these precipitates have fcc structure containing silicon, copper and magnesium atoms substituting for aluminum. Prolonged aging caused the formation of another type of precipitates with elongated shape, and they were identified to be the S″-phase. Some regions within the precipitates of the S″-phase transformed into the Q-phase with increasing silicon content in the precipitates. Precipitates of the S-phase and θ′-phase also formed by over-aging.

Original languageEnglish
Pages (from-to)291-297
Number of pages7
JournalKeikinzoku/Journal of Japan Institute of Light Metals
Volume66
Issue number6
DOIs
Publication statusPublished - 2016 Jan 1

Keywords

  • ADC12 aluminum alloy
  • Age-hardening
  • Precipitation
  • Transmission electron microscopy

ASJC Scopus subject areas

  • Mechanics of Materials
  • Mechanical Engineering
  • Metals and Alloys
  • Materials Chemistry

Fingerprint Dive into the research topics of 'Transmission electron microscopic observation of precipitates in age-hardened die-cast aluminum alloys'. Together they form a unique fingerprint.

  • Cite this