Thickness uniformity of spin coated film influenced by nonuniform temperature of substrates

Taku Ohara, Shinichiro Matsubara, Hirotoshi Kadowaki, Gota Kikugawa, Kazuhiro Takeshita, Tomoko Hamada

Research output: Contribution to journalArticlepeer-review

Abstract

The film thinning process in the spin coating has been analyzed by finite difference computational simulations. The coating liquid was assumed to be a solution of polymer solute and volatile organic solvent, for which Newtonian viscosity was given as a function of solute concentration. The flow of the coating liquid film that covers the entire substrate surface was analyzed where heat and mass transfer due to evaporation of solvent and heating/cooling by the substrate surface were taken into consideration. The whole process until all the solvent evaporates off the coating liquid and a dry coating film of the solute is left on the substrate was solved, and then the final film thickness was determined. Especially, influences of nonuniform substrate temperature on the profile of the final film thickness have been focused, for which three dimensional computational simulations have been performed. The case where the substrate is at rest and coating is processed only by drying the liquid film after a certain amount of solution liquid is deposited has also been analyzed and it was found that the final film thickness is larger at the local region of substrate with a higher temperature, exhibiting somewhat complicated thickness profiles.

Original languageEnglish
Pages (from-to)215-232
Number of pages18
JournalInternational Journal of Emerging Multidisciplinary Fluid Sciences
Volume2
Issue number4
DOIs
Publication statusPublished - 2010 Dec 1

ASJC Scopus subject areas

  • Physics and Astronomy(all)
  • Fluid Flow and Transfer Processes

Fingerprint Dive into the research topics of 'Thickness uniformity of spin coated film influenced by nonuniform temperature of substrates'. Together they form a unique fingerprint.

Cite this