Thermodynamic Structural Stability and Polarization Behavior of Cast Amorphous Alloy

Sachiko Hiromoto, Takao Hanawa, Kazuyuki Ogawa

Research output: Contribution to journalArticle

4 Citations (Scopus)

Abstract

The thermodynamic structural stability and anodic polarization behavior in Hanks' solution of cast amorphous Zr65Al7.5Ni 10Cu17.5 alloy rods with a diameter of 2.0 mm and 2.5 mm and a length of 35 mm were evaluated. The change of the magnitude of the super-cooled liquid region owing to structural relaxation was obtained from the differential scanning calorimetry (DSC) curve. Since the super-cooled liquid region of the distant region from the sprue of mold was larger than that of the proximate region to the sprue, the structural stability was lower in the distant region than in the proximate region. It was revealed that the structural stability varies along the distance from the sprue. In electrochemical analysis in a simulated body fluid, the specimens sampled from the distant region showed higher open-circuit potential, lower passive current density, and lower pitting potential than those from the proximate region. In other words, the amorphous structure with low stability shows higher passivity but lower pitting corrosion resistance than that with high stability. Consequently, the corrosion behavior of zirconium-based amorphous alloy sensitively depends on the structural stability in a biological environment.

Original languageEnglish
Pages (from-to)1824-1829
Number of pages6
JournalMaterials Transactions
Volume44
Issue number9
DOIs
Publication statusPublished - 2003 Sep
Externally publishedYes

Keywords

  • Amorphous alloy
  • Polarization behavior
  • Thermodynamic structural stability

ASJC Scopus subject areas

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering

Fingerprint Dive into the research topics of 'Thermodynamic Structural Stability and Polarization Behavior of Cast Amorphous Alloy'. Together they form a unique fingerprint.

  • Cite this