Abstract
Phases present and thermal stability of synthesized hydrides of Mg-TM-H systems (TM = Co and Ni) by preparing under a high pressure of 5 GPa using an anvil-type apparatus were studied. The MgNi2 phase with a novel crystal structure was formed at 1073 K under 5 GPa In addition, for MgH2- Ni system, two novel phases with a new composition of Mg-64 at% Ni, and Mg-55 at% Ni were formed. Using an additional hydrogen source to supply enough hydrogen, the volume fraction of the new phase with a composition of Mg-55 at%Ni increased, and the other phase vanished. This Mg-Ni-H compound was thermally stable up to 498K under an Ar atmosphere of 0.5 MPa.
| Original language | English |
|---|---|
| Pages (from-to) | 329-332 |
| Number of pages | 4 |
| Journal | Materials Science Forum |
| Volume | 350 |
| DOIs | |
| Publication status | Published - 2000 |
| Event | Proceedings of the 1st Nagaoka International Workshop on Magnesium Platform Science and Technology 2000 - Nagaoka, Jpn Duration: 2000 Jul 27 → 2000 Jul 29 |
ASJC Scopus subject areas
- Materials Science(all)
- Condensed Matter Physics
- Mechanics of Materials
- Mechanical Engineering