Thermal stability and magnetic properties of bulk amorphous Fe-Al-Ga-P-C-B-Si alloys

Akihisa Inoue, Akira Murakami, Tao Zhang, Akira Takeuchi

Research output: Contribution to journalArticlepeer-review

82 Citations (Scopus)

Abstract

The effect of Si additions on the thermal stability of the supercooled liquid before crystallization, glass-forming ability (GFA) and soft magnetic properties was examined for amorphous alloy series Fe72-xAl5Ga2P11C6B 4Six, Fe72Al5-xGa2P11C6B 4Six, Fe72Al5Ga2P11-xC6B 4Six and Fe72Al5Ga2P11-xC6-xB 4Six. The increases in the thermal stability and GFA and the improvement of soft magnetic properties were recognized in the replacements of P by 1 to 2 at%Si and of C by 1 at%Si. The supercooled liquid region (ΔTx) defined by the difference between crystallization temperature (Tx) and glass transition temperature (Tg) increases from 53 K for Fe72Al5Ga2P11C6B 4 to 58 K for Fe72Al5Ga2P11C5B 4Si1. The maximum thickness for glass formation (tmax) by copper mold casting increases from 1 mm for the Fe-Al-Ga-P-C-B alloy to 2 mm for the Fe72Al5Ga2P10C6B 4Si1 alloy. The increases in ΔTx, and tmax are presumably because of the increase in the degree of the satisfaction of the three empirical rules for the achievement of large glass-forming ability, i.e., (1) multicomponent alloy systems consisting of more than three elements, (2) significantly different atomic size ratios above about 12% and (3) negative heats of mixing. The soft magnetic properties are also improved by the replacement of 1 at%Si for P or C through the increase in the squareness ratio of B-H loop (Br/Bs) and the decrease in coercive force (Hc). The best soft magnetic properties for the bulk amorphous alloys are obtained for the Fe72Al3Ga2P10C6B 4Si1 alloy and the saturation magnetization (Bs), Hc, Br/Bs, and Curie temperature are 1.14T, 1.5 A/m, 0.45 and 594 K, respectively. The success of forming the Fe-based bulk amorphous alloys of 2 mm in thickness exhibiting the good soft magnetic properties is promising for future development as a new type of soft magnetic material.

Original languageEnglish
Pages (from-to)189-196
Number of pages8
JournalMaterials Transactions, JIM
Volume38
Issue number3
DOIs
Publication statusPublished - 1997

Keywords

  • Copper mold casting
  • Ferromagnetic bulk amorphous alloy
  • Glass transition
  • Iron-based alloy
  • Large glass-forming ability
  • Soft ferromagnetism
  • Wide supercooled liquid region

ASJC Scopus subject areas

  • Engineering(all)

Fingerprint

Dive into the research topics of 'Thermal stability and magnetic properties of bulk amorphous Fe-Al-Ga-P-C-B-Si alloys'. Together they form a unique fingerprint.

Cite this