The selective alkaline leaching of zinc oxide from Electric Arc Furnace dust pre-treated with calcium oxide

Romchat Chairaksa-Fujimoto, Katsuya Maruyama, Takahiro Miki, Tetsuya Nagasaka

Research output: Contribution to journalArticle

33 Citations (Scopus)

Abstract

Zinc ferrite (ZnFe2O4), one of the major forms of zinc in Electric Arc Furnace (EAF) dust, is very difficult to chemically dissolve in aqueous solutions. In our previous work, a pretreatment process referred to as "CaO treatment" was proposed as a key technology for transforming the ZnFe2O4 in EAF dust to ZnO and Ca2Fe2O5 without carbothermic reduction. Because this CaO treatment also enables the preferential removal of chloride, fluoride and heavy metals during heating with essentially no evaporation loss of zinc or iron, the CaO treated product, or "CaO treated dust", consists mainly of ZnO and Ca2Fe2O5, and contains no chloride, fluoride or heavy metals. Zinc leaching, which involves dissolving ZnO into either acidic or alkaline solutions, makes it possible to recover zinc from the CaO treated dust. In this study, the feasibility of the alkaline leaching of CaO treated dust was investigated using a NaOH solution for the selective leaching of zinc over iron and calcium, and the effect of temperature, reaction time, NaOH concentration and solid/liquid (S/L) ratio were examined. It was found that significantly more zinc was extracted from the CaO treated dust than the as-supplied raw dust by the NaOH solution. Nearly complete zinc extraction from the CaO treated dust was achieved without any notable dissolution of iron and calcium, which remained as Ca2Fe2O5 and Ca3Fe2(OH)12 in the leach residue. These residues can be supplied to the steel making industry as flux for the dephosphorization of hot metal or a raw material for the blast furnace.

Original languageEnglish
Pages (from-to)120-125
Number of pages6
JournalHydrometallurgy
Volume159
DOIs
Publication statusPublished - 2016 Jan 1

Keywords

  • Abbreviation EAF Electric Arc Furnace

ASJC Scopus subject areas

  • Industrial and Manufacturing Engineering
  • Metals and Alloys
  • Materials Chemistry

Fingerprint Dive into the research topics of 'The selective alkaline leaching of zinc oxide from Electric Arc Furnace dust pre-treated with calcium oxide'. Together they form a unique fingerprint.

  • Cite this