The Oxygen Content in TiC-and Ti(C,N)-base Alloys

Hisashi Suzuki, Hideaki Matsubara, Koji Hayashi

Research output: Contribution to journalArticlepeer-review

1 Citation (Scopus)

Abstract

The oxygen contents in TiC-Mo2C-Ni and Ti(G,N)-Mo2C-Ni alloy specimens (called TiC and Ti(C,N) alloys, respectively) were measured in relation to the carbon content of alloys and sintering conditions. Specimens were mainly in vacuum sintered. It was found that the oxygen contents of both alloys were markedly decreased to the value as small as about 0.1%, with increasing carbon content. The oxygen content of Ti(C,N) alloy was much lower, especially, in low carbon alloy, than that of TiC alloy. This result was considered to be due to the fact that the amount of oxygen absorbed during the process before sintering was smaller in Ti(C, N) powder because of its high resistance to oxidation.

Original languageEnglish
Pages (from-to)290-293
Number of pages4
Journaljournal of the japan society of powder and powder metallurgy
Volume29
Issue number8
DOIs
Publication statusPublished - 1982 Jan
Externally publishedYes

ASJC Scopus subject areas

  • Mechanical Engineering
  • Industrial and Manufacturing Engineering
  • Metals and Alloys
  • Materials Chemistry

Fingerprint

Dive into the research topics of 'The Oxygen Content in TiC-and Ti(C,N)-base Alloys'. Together they form a unique fingerprint.

Cite this