The evolution of martensitic transformation in Ni-Mn-Ga/Al2O3 polycrystalline 100-nm – 2-μm films with Ni- and Ga-excess

S. Shevyrtalov, H. Miki, M. Ohtsuka, V. Khovaylo, V. Rodionova

Research output: Contribution to journalArticle

1 Citation (Scopus)

Abstract

Polycrystalline Ni54Mn18Ga28 films with thicknesses ranging from 100-nm to 2-μm were fabricated by deposition on alumina ceramic substrates; bulk and surface properties were then characterized by structural and magnetic methods. The evolution of martensitic transformation of the films was studied. Both martensitic transformation and Curie temperature were found to be above room temperature, with the former overlapping the latter when films thicker than 100-nm were used. Static magnetic properties revealed the presence of strong internal stresses in the films, thus influencing coercive force value which changes with the increase in thickness. A distinct presence of martensitic twinning at room temperature was revealed, which started with the 400-nm film and increased with the 1- and 2-μm films. A maze-like domain structure (without correlation to the surface features), was found in the 1- and 2-μm films. A strong dependence between crystallites and magnetic domains was discovered in films ranging from 100- to 400-nm. A nonlinear dependence of the domain width on the film thickness was also observed, which converges with the coercive force dependence.

Original languageEnglish
Pages (from-to)538-543
Number of pages6
JournalJournal of Alloys and Compounds
Volume767
DOIs
Publication statusPublished - 2018 Oct 30

Keywords

  • Heusler alloys
  • Magnetic properties
  • Martensitic transformation
  • Ni-Mn-Ga film
  • Thin films

ASJC Scopus subject areas

  • Mechanics of Materials
  • Mechanical Engineering
  • Metals and Alloys
  • Materials Chemistry

Fingerprint Dive into the research topics of 'The evolution of martensitic transformation in Ni-Mn-Ga/Al<sub>2</sub>O<sub>3</sub> polycrystalline 100-nm – 2-μm films with Ni- and Ga-excess'. Together they form a unique fingerprint.

  • Cite this