TY - JOUR
T1 - Tensile Properties and Surface Reaction Layer of Biomaterial, Ti-29Nb-13Ta-4.6Zr, Cast by Dental Precision Casting Process Using Various Investment Materials
AU - Niinomi, Mitsuo
AU - Akahori, Toshikazu
AU - Manabe, Tetsunori
AU - Takeuchi, Tsutomu
AU - Katsura, Shigeki
AU - Fukui, Hisao
AU - Suzuki, Akihiro
N1 - Copyright:
Copyright 2017 Elsevier B.V., All rights reserved.
PY - 2004/3
Y1 - 2004/3
N2 - Ti-29Nb-13Ta-4.6Zr for biomedical applications and conventional α+β type titanium Ti-6Al-4V ELI for biomedical and dental applications are subjected to dental precision casting using commercial alumina based and magnesia based investment materials, and modified magnesia based investment material. Mechanical properties and surface reaction layers of cast Ti-29Nb-13Ta-4.6Zr were investigated in order to find the suitable investment material for dental precision casting of Ti-29Nb-13Ta-4.6Zr in comparison with Ti-6Al-4V ELI. The following results were obtained. Elongation of Ti-29Nb-13Ta-4.6Zr cast into commercial alumina based investment material is lower than those cast into commercial magnesia and modified magnesia based investment materials although no big difference in strength is obtained regardless of the investment materials. The formation of surface reaction layer composed of oxide and α-case is restrained by magnesia and modified magnesia based investment materials as compared with alumina based one. The modified magnesia based investment material is better for casting of Ti-29Nb-13Ta-4.6Zr as compared with magnesia and alumina based investment materials.
AB - Ti-29Nb-13Ta-4.6Zr for biomedical applications and conventional α+β type titanium Ti-6Al-4V ELI for biomedical and dental applications are subjected to dental precision casting using commercial alumina based and magnesia based investment materials, and modified magnesia based investment material. Mechanical properties and surface reaction layers of cast Ti-29Nb-13Ta-4.6Zr were investigated in order to find the suitable investment material for dental precision casting of Ti-29Nb-13Ta-4.6Zr in comparison with Ti-6Al-4V ELI. The following results were obtained. Elongation of Ti-29Nb-13Ta-4.6Zr cast into commercial alumina based investment material is lower than those cast into commercial magnesia and modified magnesia based investment materials although no big difference in strength is obtained regardless of the investment materials. The formation of surface reaction layer composed of oxide and α-case is restrained by magnesia and modified magnesia based investment materials as compared with alumina based one. The modified magnesia based investment material is better for casting of Ti-29Nb-13Ta-4.6Zr as compared with magnesia and alumina based investment materials.
KW - Dental precision casting
KW - Investment material
KW - Mechanical properties
KW - Surface reaction layer
KW - β type titanium alloy
UR - http://www.scopus.com/inward/record.url?scp=2142808836&partnerID=8YFLogxK
UR - http://www.scopus.com/inward/citedby.url?scp=2142808836&partnerID=8YFLogxK
U2 - 10.2355/tetsutohagane1955.90.3_154
DO - 10.2355/tetsutohagane1955.90.3_154
M3 - Article
AN - SCOPUS:2142808836
VL - 90
SP - 154
EP - 161
JO - Tetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan
JF - Tetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan
SN - 0021-1575
IS - 3
ER -