Temperature dependent control of the solubility of gallium nitride in supercritical ammonia using mixed mineralizer

Daisuke Tomida, Kiyoshi Kuroda, Kentaro Nakamura, Kun Kyo, Chiaki Yokoyama

Research output: Contribution to journalArticle

1 Citation (Scopus)

Abstract

Using a mass-loss method, we investigated the solubility change of gallium nitride (GaN) in supercritical ammonia with mixed mineralizers [ammonium chloride (NH4Cl)+ammonium bromide (NH4Br) and NH4Cl+ammonium iodide (NH4I)]. The solubilities were measured over the temperature range 450-550°C, at 100MPa. The solubility increased with NH4Cl mole fraction at 450°C and 100MPa. The temperature dependence of the solubility curve was then measured at an equal mole ratio of the two mineralizers. The slope of the solubility-temperature relationship in the mixed mineralizer was between those of the individual mineralizers. These results show that the temperature dependence of the solubility of GaN can be controlled by the mineralizer mixture ratio. The results of the van't Hoff plot suggest that the solubility species were unchanged over the investigated temperature range. Our approach might pave the way to realizing large, high-quality GaN crystals for future gallium-nitride electronic devices, which are increasingly on demand in the information-based age.

Original languageEnglish
Article number127
JournalChemistry Central Journal
Volume12
Issue number1
DOIs
Publication statusPublished - 2018 Dec 3

Keywords

  • Acidic mineralizer
  • Ammonothermal
  • Gallium nitride
  • Solubility
  • Supercritical ammonia

ASJC Scopus subject areas

  • Chemistry(all)

Fingerprint Dive into the research topics of 'Temperature dependent control of the solubility of gallium nitride in supercritical ammonia using mixed mineralizer'. Together they form a unique fingerprint.

  • Cite this