Synthesizing of nanocomposite WC/MgO powders by mechanical solid-state reduction and subsequent plasma-activated sintering

M. Sherif El-Eskandarany, M. Omori, T. J. Konno, K. Sumiyama, T. Hirai, K. Suzuki

Research output: Contribution to journalArticlepeer-review

22 Citations (Scopus)

Abstract

A ceramic/ceramic nanocomposite powder of WC/MgO has been fabricated by high-energy ball milling a mixture of elemental Mg and powders of C with WO 3 under an argon gas atmosphere at room temperature. During the early stage of milling (at 1.8 ks), the WO 3 and C powders are embedded into the soft matrix of Mg (the reducing agent) particles to form coarse composite powders of the reactant materials. Increasing the milling time (to 22 ks) leads to the formation of fresh active surfaces of Mg, which have a high reducing potential and react with the WO 3 in a typical oxidation/reduction reaction. At the end of this stage (at 43 ks), the Mg powders are oxidized to MgO, whereas the WO 3 is reduced completely to metallic W. During the last stage of milling (86 to 173 ks), a solid-state reaction takes place between W and the unreacted C powders to yield nanocomposite WC/MgO particles. This end-product was consolidated in vacuum at 1963 K with a pressure of 19.6 to 38.2 MPa for 0.3 ks, using a plasma-activated sintering (PAS) method. The sintered sample is fully dense (above 99.5 pct of the theoretical density) and contains nanocrystalline grains of less than 50 nm in diameter. This fine grain structure offers an opportunity for the composite material to combine high values of two opposite properties, i.e., hardness and fracture toughness (K c), of 15 GPa and 14 MPa√m, respectively. Here, we propose this nanocomposite material for a wide range of industrial applications, including tips for cutting tools and tips for oil drilling equipment.

Original languageEnglish
Pages (from-to)157-164
Number of pages8
JournalMetallurgical and Materials Transactions A: Physical Metallurgy and Materials Science
Volume32
Issue number1
Publication statusPublished - 2001 Jan 1
Externally publishedYes

ASJC Scopus subject areas

  • Condensed Matter Physics
  • Mechanics of Materials
  • Metals and Alloys

Fingerprint Dive into the research topics of 'Synthesizing of nanocomposite WC/MgO powders by mechanical solid-state reduction and subsequent plasma-activated sintering'. Together they form a unique fingerprint.

Cite this