Synthesis of magnetite particles by oxidation of hydroxyl-chloride green rust suspension under controlled conditions

Aya Yoshino, Shun Fujieda, Kozo Shinoda, Shigeru Suzuki

Research output: Contribution to journalArticle

Abstract

Magnetite (Fe3O4) particles were synthesized by oxidation of a hydroxyl chloride green rust (GR(Cl-)) suspension at room temperature. The formation process of Fe3O4 particles was characterized by X-ray diffraction, magnetization and electrochemical measurements. The results showed that a small amount of fine Fe 3O4 particles were nucleated when the supernatant solution of the as-synthesized GR(Cl-) suspension was replaced by deaerated water. By controlling the injection of oxygen gas at room temperature, Fe 3O4 particles of about 70 nm in diameter formed from such GR(Cl-) suspension, while goethite (α-FeOOH) particles were mainly obtained from the as-synthesized GR(Cl-) suspension under the same oxidation conditions. Hence, the saturation magnetization of final oxidation products obtained from the GR(Cl-) suspension in which the supernatant solution was replaced was about 60 emu/g, which was six times larger than that obtained from the as-synthesized GR(Cl-) suspension. In the early stage of the oxidation process, the oxidation-reduction potential (ORP) in the GR(Cl-) suspension in which supernatant solution was replaced was lower than that in the as-synthesized GR(Cl-) suspension. In addition, the value of pH of the former suspension was higher than that of the latter suspension. It is concluded that the formation of Fe3O4 particles is enhanced in solution with relatively low ORP and high pH.

Original languageEnglish
Pages (from-to)894-899
Number of pages6
JournalIsij International
Volume53
Issue number5
DOIs
Publication statusPublished - 2013 Jun 26

Keywords

  • Green rust
  • Magnetite

ASJC Scopus subject areas

  • Mechanical Engineering
  • Mechanics of Materials
  • Materials Chemistry
  • Metals and Alloys

Fingerprint Dive into the research topics of 'Synthesis of magnetite particles by oxidation of hydroxyl-chloride green rust suspension under controlled conditions'. Together they form a unique fingerprint.

  • Cite this