Synthesis of filled skutterudite compounds: BayFexCo4-xSb12

L. Chen, X. Tang, T. Goto, T. Hirai

Research output: Contribution to journalArticlepeer-review

44 Citations (Scopus)

Abstract

Ba-filled skutterudite compounds, BayFexCo4-xSb12, were synthesized by a two-step solid reaction method. A binary compound of Sb3Ba and a ternary compound of FexCo1-xSb2 were first synthesized at 900 and 973 K, respectively. The presynthesized Sb3Ba and FexCO1-xSb2 were then mixed with Sb and heated at 973 K in an Ar atmosphere. The resulting powder was of single phase with a composition of BayFexCo4-xSb12, having skutterudite structure with the Sb-dodecahedron voids fractionally filled by Ba. The lattice constant of BayFexCo4-xSb12 increased with Ba and Fe content. The maximum filling fraction of Ba (ymax) in BayFexCo4-xSb12 was found to be greater than that of Ce or La in LnyFexCo4-xSb12, especially in the lower Fe content region. The ymax varied from 0.35 to near 1.0 when Fe content (x) changed from 0 to 4.

Original languageEnglish
Pages (from-to)2276-2279
Number of pages4
JournalJournal of Materials Research
Volume15
Issue number11
DOIs
Publication statusPublished - 2000 Nov

ASJC Scopus subject areas

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering

Fingerprint

Dive into the research topics of 'Synthesis of filled skutterudite compounds: Ba<sub>y</sub>Fe<sub>x</sub>Co<sub>4-x</sub>Sb<sub>12</sub>'. Together they form a unique fingerprint.

Cite this