Synthesis of chalcopyrite-type CuInSe2 nanoparticles from aqueous solution at room temperature

Shi Na Li, Rui Xin Ma, Chun Hong Ma, Kai Huang, Dong Ran Li, Yu Qin Xiao, Liang Wei He, Hong Min Zhu

Research output: Contribution to journalArticle

4 Citations (Scopus)

Abstract

Chalcopyrite-type CuInSe2 (CIS) nanoparticles were successfully synthesized by Se powder, CuCl, and InCl3 as raw materials and water as solvent at room temperature based on the principles of simultaneous equilibrium. The size of nanoparticles ranges from 20 to 50 nm in diameter. The crystalline structure and morphology of the CIS nanoparticles were characterized by means of X-ray diffraction (XRD), X-ray photoelectron spectroscopy analysis (XPS), and transmission electron microscopy (TEM). The CIS nanoparticles were further enhanced after heat treatment at 500 °C for 2 h. The CIS film was fabricated by a mixture of CIS nanoparticles and novolac resin with a weight percentage of 30% by spin coating. The photoelectrical properties of such CIS films were measured and the results show an incident light density of 7.63 mW cm-2 with the bias voltage of 0.4 V, and the current density could approach 4.10 mA/cm2 giving an on/off switching ratio of 2.0.

Original languageEnglish
Pages (from-to)51-53
Number of pages3
JournalMaterials Letters
Volume101
DOIs
Publication statusPublished - 2013 Jan 1
Externally publishedYes

Keywords

  • Aqueous-solution
  • Photoelectrical properties
  • Room temperature

ASJC Scopus subject areas

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering

Fingerprint Dive into the research topics of 'Synthesis of chalcopyrite-type CuInSe<sub>2</sub> nanoparticles from aqueous solution at room temperature'. Together they form a unique fingerprint.

  • Cite this