TY - JOUR
T1 - Superconducting properties in Sr-La-Co-O system
AU - Sait, Yoshitami
AU - Noji, Takashi
AU - Endo, Akihiko
AU - Matsuzaki, Nozomu
AU - Katsumata, Masao
AU - Higuchi, Naoaki
PY - 1987/4
Y1 - 1987/4
N2 - The dependence of Tc of the superconducting ceramics SrxLa2-xCuO4 was measured on the sintering conditions, temperature and time, on the cooling rate after annealing and on the depth from the initial surface of the sample. The sintering temperature 1050C was better than 1000C and the sintering for five hours was the best one. There was no difference between the superconductivity of the initial surface and of the inside of the sample.
AB - The dependence of Tc of the superconducting ceramics SrxLa2-xCuO4 was measured on the sintering conditions, temperature and time, on the cooling rate after annealing and on the depth from the initial surface of the sample. The sintering temperature 1050C was better than 1000C and the sintering for five hours was the best one. There was no difference between the superconductivity of the initial surface and of the inside of the sample.
UR - http://www.scopus.com/inward/record.url?scp=0023326956&partnerID=8YFLogxK
UR - http://www.scopus.com/inward/citedby.url?scp=0023326956&partnerID=8YFLogxK
U2 - 10.1143/JJAP.26.L491
DO - 10.1143/JJAP.26.L491
M3 - Article
AN - SCOPUS:0023326956
VL - 26
SP - L491-L492
JO - Japanese Journal of Applied Physics, Part 1: Regular Papers & Short Notes
JF - Japanese Journal of Applied Physics, Part 1: Regular Papers & Short Notes
SN - 0021-4922
IS - 4 A
ER -