Structural studies of a mixed-valence state in the incommensurate composite crystal Sr1.261CoO3

Masaaki Isobe, Hiroyuki Yoshida, Eiji Takayama Muromachi, Kenji Ohoyama

Research output: Contribution to journalArticlepeer-review

2 Citations (Scopus)

Abstract

The incommensurate modulated crystal structure of the hexagonal cobalt oxide Sr1.261CoO3 has been studied using a four-dimensional (4D) superspace profile analysis of neutron powder diffraction data. Sr1.261CoO3 is a composite crystal that consists of the [CoO3] and [2Sr] subsystems. The [CoO3] subsystem forms 1D chains that run parallel to the c-axis and consist of face-sharing CoO6 polyhedra with octahedral (Oh) and trigonal prismatic (TP) coordinations. The structure analysis reveals that the [CoO3] chains contain 73.9% Oh and 26.1% TP sites, and that the TP sites have longer Co-O bonds than the Oh sites: dav. = 2.039(4)Å (TP) and 1.895(3)Å (Oh). The averaged Co bond valences are Co3.56(3)+ in the Oh sites and Co2.45(3)+ in the TP sites, suggesting that a considerable amount of Co3+ ions mixed with Co4+ions in the Oh sites and with Co2+ ions in the TP sites. The observed magnetic susceptibility can be well explained assuming that the compound has the Co mixed-valence state with the spin configurations of S = 0 low-spin state for Co3+(dε6), S = 1/2 low-spin state for Co 4+(dε5) and S = 3/2 high-spin state for Co 2+(dε5). The Weiss temperature, approximately 0.8 K, implies that Sr1.261CoO3 naturally assumes a Curie paramagnetic state, probably owing to the obstruction of the intrachain magnetic interaction by the nonmagnetic Co3+ ions. These results suggest that the nonmagnetic Co3+ ions play an essential role in the magnetism of Sr CoO3 systems.

Original languageEnglish
Article number065004
JournalScience and Technology of Advanced Materials
Volume11
Issue number6
DOIs
Publication statusPublished - 2010 Dec

ASJC Scopus subject areas

  • Materials Science(all)

Fingerprint

Dive into the research topics of 'Structural studies of a mixed-valence state in the incommensurate composite crystal Sr<sub>1.261</sub>CoO<sub>3</sub>'. Together they form a unique fingerprint.

Cite this