Stress/strain characteristics of Cu-alloy sheath MgB2 superconducting wires

Kazumune Katagiri, Koichi Kasaba, Yoshitaka Shoji, Daisuke Yamakage, Takeshi Obara, Satoshi Shimura, Naoki Koshizuka, Kazuo Watanabe

Research output: Contribution to journalArticlepeer-review

8 Citations (Scopus)

Abstract

The mechanical properties of Cu and Cu-alloy (Cu-Zr, Cu-Be and Cu-Cr) sheath in situ PIT-processed MgB2 superconducting wires were studied at room temperature (RT) and 4.2 K. The effects of stress/strain on the critical current (Ic) of the wires have also been studied at 4.2 K and in magnetic fields up to 5 T. Alloying the Cu sheath significantly increased the yield stress of the wires. The 0.5% flow stresses of the Cu-alloy sheath wires were 147-237 MPa, whereas that of Cu was 55 MPa. At RT, the serration in the stress-strain curves corresponding to the multiple cracking was observed around a strain of 0.4% and the curve almost saturated beyond that point. The strain dependence of Ic prior to the critical strain (εirr) was different depending on the magnetic field; being almost constant at 2 T and increased with strain at 5 T. The Ic decreased beyond εirr, which was much larger for Cu-alloy sheath wires as compared with Cu sheath wire. The magnitude of εirr is due to the difference in the thermal compressive strain in the MgB2 core, which was relaxed by yielding in the sheath materials. The transverse compression tests revealed that the Ic of the Cu-alloy sheath wire did not degrade up to about 95 MPa, which is also higher than that of Cu sheath wire.

Original languageEnglish
Pages (from-to)220-224
Number of pages5
JournalCryogenics
Volume47
Issue number4
DOIs
Publication statusPublished - 2007 Apr

Keywords

  • Critical current (C)
  • Cu-alloy sheath (A)
  • Mechanical properties (C)
  • PIT MgB wires (A)
  • Stress/strain effects (C)

ASJC Scopus subject areas

  • Materials Science(all)
  • Physics and Astronomy(all)

Fingerprint Dive into the research topics of 'Stress/strain characteristics of Cu-alloy sheath MgB<sub>2</sub> superconducting wires'. Together they form a unique fingerprint.

Cite this