STRENGTH OF TiC//0//. //5N//0//. //5-Mo//2C-Ni ALLOY IN RELATION TO THE MICROSTRUCTURAL DEFECTS.

Hisashi Suzuki, Hideaki Matsubara, Takeshi Saitoh

Research output: Contribution to journalArticlepeer-review

12 Citations (Scopus)

Abstract

The transverse-rupture strength of an alloy sintered in nitrogen, HIP-treated in argon and resintered in nitrogen at 1723-1823 K was studied. Pores were observed in specimens sintered in nitrogen. During HIP, the pores changed to nickel pools resulting in increase in strength. The nickel pools changed to pores when specimens were resintered. The strength of specimens resintered at a higher temperature showed a strength as high as 3. 2 GPa.

Original languageEnglish
Pages (from-to)1011-1016
Number of pages6
JournalNippon Kinzoku Gakkai-si
Volume48
Issue number10
Publication statusPublished - 1984 Dec 1
Externally publishedYes

ASJC Scopus subject areas

  • Condensed Matter Physics
  • Mechanics of Materials
  • Metals and Alloys
  • Materials Chemistry

Fingerprint Dive into the research topics of 'STRENGTH OF TiC//0//. //5N//0//. //5-Mo//2C-Ni ALLOY IN RELATION TO THE MICROSTRUCTURAL DEFECTS.'. Together they form a unique fingerprint.

Cite this