Soft magnetic properties and microstructure of NiFe(Cr)/FeCo/NiFe(Cr) films with large saturation magnetization

H. Katada, T. Shimatsu, I. Watanabe, H. Muraoka, Y. Nakamura

Research output: Contribution to journalConference article

22 Citations (Scopus)

Abstract

The soft magnetic properties of FeCo films, sandwiched by thin NiFe or NiFeCr films, are discussed in relation to the microstructure. Ta/NiFe(Cr)(5 nm)/FeCo(100 nm)/NiFe(Cr)(5 nm)/Ta films prepared using the UHV sputtering process with pure Ar plasma show bcc-(110) preferred grain orientation of FeCo layer with the 〈110〉 direction sharply perpendicular to the film plane, resulting in soft magnetic properties. No significant difference in soft magnetic properties was observed by the use of nonmagnetic NiFeCr layers instead the NiFe layers, moreover, by varying FeCo composition between 25 and 30 at%Co. The best thickness of the FeCo layer in order to realize soft magnetic properties was found to be ∼ 100 mn in the present study, with a high saturation magnetization of 2.3 T. An addition of N2 gas to Ar plasma during film deposition did not lead to an improvement of the soft magnetic properties. A film of [FeCo(100 nm)/NiFe(5 nm)4 layer structure was subjected to the fabrication of single-pole-type recording head, and it is successfully demonstrated that the film has a sufficient softness to be used for the recording head application.

Original languageEnglish
Pages (from-to)2225-2227
Number of pages3
JournalIEEE Transactions on Magnetics
Volume38
Issue number5 I
DOIs
Publication statusPublished - 2002 Sep 1
Event2002 International Magnetics Conference (Intermag 2002) - Amsterdam, Netherlands
Duration: 2002 Apr 282002 May 2

Keywords

  • FeCo films
  • Lattice strain
  • Preferred grain orientation
  • Saturation magnetization
  • Soft magnetic properties

ASJC Scopus subject areas

  • Electronic, Optical and Magnetic Materials
  • Electrical and Electronic Engineering

Fingerprint Dive into the research topics of 'Soft magnetic properties and microstructure of NiFe(Cr)/FeCo/NiFe(Cr) films with large saturation magnetization'. Together they form a unique fingerprint.

  • Cite this