Sintering and characterization of er2ba2cu1.1pt0.9o8 compacts

Toetsu Shishido, Yoko Saito, Tsuguo Fukuda, Naoki Toyota, Takahiko Sasaki, Hideo Iwasaki, Kazutoshi Ukei

Research output: Contribution to journalArticlepeer-review

2 Citations (Scopus)


Er2Ba2Cu1.1Pt0.9O8 was synthesized successfully by a direct-reaction sintering method with raw materials. Fractured surfaces of sintered compacts are observed. The densities of the specimens sintered at 1400ºC are 79.0% of the theoretical density, 8.56 Mgµm-3. Above T≃20 K, the magnetic susceptibility of this compound follows the Curie-Weiss law.

Original languageEnglish
Pages (from-to)L1926-L1928
JournalJapanese journal of applied physics
Issue number10 A
Publication statusPublished - 1988 Oct


  • Er2Ba2Cu
  • Magnetic properties
  • Orthorhombic phase
  • Pt complex oxide
  • Pto 908
  • Sintered compacts

ASJC Scopus subject areas

  • Engineering(all)
  • Physics and Astronomy(all)


Dive into the research topics of 'Sintering and characterization of er2ba2cu1.1pt0.9o8 compacts'. Together they form a unique fingerprint.

Cite this