Resistive non-volatile memories fabricated with poly(vinylidene fluoride)/poly(thiophene) blend nanosheets

Huie Zhu, Shunsuke Yamamoto, Jun Matsui, Tokuji Miyashita, Masaya Mitsuishi

    Research output: Contribution to journalArticlepeer-review

    8 Citations (Scopus)

    Abstract

    Ferroelectric poly(vinylidene fluoride)/semiconductive polythiophene (P3CPenT) blend monolayers were developed at varying blend ratios using the Langmuir-Blodgett technique. The multilayered blend nanosheets show much improved surface roughness that is more applicable for electronics applications than spin-cast films. Because of the precisely controllable bottom-up construction, semiconductive P3CPenT were well dispersed into the ferroelectric PVDF matrix. Moreover, the ferroelectric matrix contains almost 100% β crystals: a polar crystal phase responsible for the ferroelectricity of PVDF. Both the good dispersion of semiconductive P3CPenT and the outstanding ferroelectricity of the PVDF matrix in the blend nanosheets guaranteed the success of ferroelectric organic non-volatile memories based on ferroelectricity-manipulated resistive switching with a fresh high ON/OFF ratio and long endurance to 30 days.

    Original languageEnglish
    Pages (from-to)7963-7968
    Number of pages6
    JournalRSC Advances
    Volume8
    Issue number15
    DOIs
    Publication statusPublished - 2018

    ASJC Scopus subject areas

    • Chemistry(all)
    • Chemical Engineering(all)

    Fingerprint

    Dive into the research topics of 'Resistive non-volatile memories fabricated with poly(vinylidene fluoride)/poly(thiophene) blend nanosheets'. Together they form a unique fingerprint.

    Cite this