Rational Route for Increasing Intercalation Capacity of Hard Carbons as Sodium-Ion Battery Anodes

Research output: Contribution to journalArticlepeer-review

1 Citation (Scopus)

Abstract

Hard carbon (HC) is the most promising candidate for sodium-ion battery anode materials. Several material properties such as intensity ratio of the Raman spectrum, lateral size of HC crystallite (La), and interlayer distance (d002) have been discussed as factors affecting anode performance. However, these factors do not reflect the bulk property of the Na+ intercalation reaction directly, since Raman analysis has high surface sensitivity and La and d002 provide only one-dimensional crystalline information. Herein, it was proposed that the crystallite interlayer area (Ai) defined using La, d002, and stacking height (Lc) governs Na+ intercalation behavior of various HCs. It was revealed that various wood-derived HCs exhibited the similar total capacity of approximately 250 mAh g−1, whereas the Na+ intercalation capacity (Ci) was proportional to Ai with the correlation coefficient of R2=0.94. The evaluation factor of Ai was also adaptable to previous reports and strongly correlated with their Ci, indicating that Ai is more widely adaptable than the conventional evaluation methods.

Original languageEnglish
Pages (from-to)5762-5768
Number of pages7
JournalChemSusChem
Volume13
Issue number21
DOIs
Publication statusPublished - 2020 Nov 6

Keywords

  • battery
  • carbon
  • electrochemistry
  • ion storage
  • sodium

ASJC Scopus subject areas

  • Environmental Chemistry
  • Chemical Engineering(all)
  • Materials Science(all)
  • Energy(all)

Fingerprint Dive into the research topics of 'Rational Route for Increasing Intercalation Capacity of Hard Carbons as Sodium-Ion Battery Anodes'. Together they form a unique fingerprint.

Cite this