Properties of Ni2MnGa shape memory alloy prepared by spark plasma sintering

Z. Wang, M. Matsumoto, T. Abe, K. Oikawa, J. Qiu, T. Takagi, J. Tani

Research output: Contribution to journalConference articlepeer-review

9 Citations (Scopus)

Abstract

Preparation of Ni2MnGa shape memory alloys (SMA) by Spark Plasma Sintering (SPS) and property comparisons of sintered alloys to arc-melted alloys are investigated. The Ni2MnGa alloy with relative density of 99.6% is obtained with a maximum pressure of 80 MPa and a maximum temperature of 1173 K applied in the sintering process. Heat treatment is subsequently performed at 1073 K for 864 ks in vacuum and slowly cooled. The martensitic transformation temperatures, Ms, Mf, As, Af, are determined as 235 K, 220 K, 239 K and 254 K respectively. The elastic moduli and Poisson ratio are 107.9 GPa and 0.38 respectively. Tensile and compression tests are conducted at room temperature. The tensile fracture strength is increased in sintered alloys. For compression tests, sintered alloys show compressive ductility of 14.2% with transgranular cracking while arc-melted alloys only have 1.5% plastic deformation and both intergranular cracking and transgranular cracking. Furthermore, the sintered alloys possess higher yield stresses and fracture strengths.

Original languageEnglish
Pages (from-to)489-492
Number of pages4
JournalMaterials Science Forum
Volume327
Publication statusPublished - 2000
EventProceedings of the 1999 International Symposium and Exhibition on Shape Memory Materials (SMM'99) - Kanazawa, Jpn
Duration: 1999 May 191999 May 21

ASJC Scopus subject areas

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering

Fingerprint

Dive into the research topics of 'Properties of Ni<sub>2</sub>MnGa shape memory alloy prepared by spark plasma sintering'. Together they form a unique fingerprint.

Cite this