Preparation of silica-coated Co-Pt alloy nanoparticles

Yoshio Kobayashi, Mitsuru Horie, Daisuke Nagao, Yasuo Ando, Terunobu Miyazaki, Mikio Konno

Research output: Contribution to journalArticlepeer-review

19 Citations (Scopus)

Abstract

A previously proposed method for silica-coating of Co nanoparticles was extended to silica-coating of Co-Pt alloy nanoparticles. The alloy nanoparticles were prepared from CoCl2 (1.2 × 10- 3 M), H2PtCl6 (1.2 × 10- 3 M), citric acid (4 × 10- 4 M) and NaBH4 (1.2 × 10- 2 M). The silica-coating was performed in aqueous/ethanolic solution with a silane coupling agent, 3-aminopropyltrimethoxysilane (8 × 10- 5 M), and a silica source, tetraethoxyorthosilicate (7.2 × 10- 4 M) in the presence of the alloy nanoparticles. TEM observation and X-ray diffraction measurements revealed that the alloy nanoparticles were coated with silica and consisted of fcc Co-Pt alloy crystallites with crystal sizes of 4.6-10.7 nm. Magnetic properties of the silica-coated particles were strongly dependent on annealing temperature. Maximum values of 1.4 emu/g-sample for saturation magnetization and 450 Oe for coercive field were obtained for the particles annealed at 300 °C. Annealing above 300 °C transformed the crystallite from the alloy to pure Pt probably through oxidation of cobalt in the alloy, resulting in reductions in saturation magnetization and coercive field.

Original languageEnglish
Pages (from-to)2046-2049
Number of pages4
JournalMaterials Letters
Volume60
Issue number16
DOIs
Publication statusPublished - 2006 Jul

Keywords

  • Composite materials
  • Magnetic materials
  • Metals and alloys
  • Nanocomposites
  • Nanomaterials
  • Sol-gel preparation

ASJC Scopus subject areas

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering

Fingerprint Dive into the research topics of 'Preparation of silica-coated Co-Pt alloy nanoparticles'. Together they form a unique fingerprint.

Cite this