Preparation of lithium manganese oxide fine particles by spray pyrolysis and their electrochemical properties

Y. Iriyama, Y. Tachibana, R. Sasasoka, N. Kuwata, T. Abe, M. Inaba, A. Tasaka, K. Kikuchi, J. Kawamura, Z. Ogumi

Research output: Contribution to journalArticlepeer-review

7 Citations (Scopus)

Abstract

Highly crystalline nano-sized lithium manganese oxide particles were fabricated by spray pyrolysis. The resultant particles had well-developed facet planes in a transmission electron microscopy (TEM) image and electron diffraction pattern from a single particle also showed clear diffraction spots, indicating that the prepared particles were highly crystalline. The mean crystallite size estimated from X-ray diffraction peaks was ca. 18 nm, which was in good agreement with the diameter of the particles observed in the TEM image. These particles were gathered on platinum mesh and their electrochemical properties were investigated. The mean crystallite size increased with an increase in annealing temperature, which influenced the electrochemical lithium insertion/extraction properties of the particles. In particular, samples annealed at 773 K showed different kinds of lithium extraction/insertion properties in the cyclic voltammogram (CV), and only a couple of broad redox peaks were observed at around 0.8 V (versus Ag/AgCl) between 0.4 and 1.0 V. It is suggested that lithium distribute randomly in the sample annealed at 773 K sample due to the effects of grain boundaries, which resulted in different kinds of phase transition reactions.

Original languageEnglish
Pages (from-to)1057-1062
Number of pages6
JournalJournal of Power Sources
Volume174
Issue number2
DOIs
Publication statusPublished - 2007 Dec 6

Keywords

  • Fine particles
  • Lithium manganese oxide
  • Phase transition
  • Rechargeable lithium batteries

ASJC Scopus subject areas

  • Renewable Energy, Sustainability and the Environment
  • Energy Engineering and Power Technology
  • Physical and Theoretical Chemistry
  • Electrical and Electronic Engineering

Fingerprint Dive into the research topics of 'Preparation of lithium manganese oxide fine particles by spray pyrolysis and their electrochemical properties'. Together they form a unique fingerprint.

Cite this