Preparation of fine Nb3Al powder by hydriding and dehydriding in an arc-melting chamber

X. G. Li, A. Chiba, K. Ohsaki, Y. Morita, M. Uda

Research output: Contribution to journalArticlepeer-review

24 Citations (Scopus)

Abstract

The disintegration due to hydrogenation of Nb-Al alloys with eight different compositions has been studied. The hydrogenation is performed directly in an arc-melting chamber without exposing Nb-Al ingots to air after arc-melting. Because the active surface resulting from arc-melting is preserved, Nb-Al alloys absorb a large amount of hydrogen and disintegrate rapidly into fine particles, even though the pressure of hydrogen is only at 0.1 MPa. This disintegration is closely related to the arc-melting atmosphere and the composition of the alloys. Structural changes of Nb-Al alloys before and after hydrogenation and dehydrogenation have been examined by X-ray diffraction, electron microscopy and chemical analysis. A fine powder of single Nb3Al phase with an average particle size of less than 14 μm can easily be obtained by hydriding Nb-Al alloy buttons with aluminum compositions from 22 to 28 at.% in an arc-melting chamber, followed by dehydrogenation at 1073 K for 3.6 ks.

Original languageEnglish
Pages (from-to)202-209
Number of pages8
JournalJournal of Alloys and Compounds
Volume238
Issue number1-2
DOIs
Publication statusPublished - 1996 May 1
Externally publishedYes

Keywords

  • Hydrogenation
  • Intermetallic compounds
  • NbAl
  • Powder metallurgy
  • X-ray diffraction

ASJC Scopus subject areas

  • Mechanics of Materials
  • Mechanical Engineering
  • Metals and Alloys
  • Materials Chemistry

Fingerprint Dive into the research topics of 'Preparation of fine Nb<sub>3</sub>Al powder by hydriding and dehydriding in an arc-melting chamber'. Together they form a unique fingerprint.

Cite this