Preparation and tribological properties of SiC/rice bran carbon composite ceramics

You Zhou, Kiyoshi Hirao, Takeshi Yamaguchi, Kazuo Hokkirigawa

Research output: Contribution to journalArticlepeer-review

11 Citations (Scopus)

Abstract

Silicon carbide (SiC) ceramics have good wear resistance but poor friction properties under dry sliding conditions. To lower the friction of SiC, a novel porous carbon material called rice bran carbon (RBC) was added into SiC to make SiC/RBC composite ceramics. The SiC/RBC composites were prepared by mixing one of three kinds of RBC powders having different particle sizes and a fine SiC doped with Al4C3 and B4C additives and sintering at 1600 °C for 5 min by a pulse electric current sintering (PECS) method. The mechanical and tribological properties of the SiC/RBC composites were evaluated and compared with those of monolithic SiC, monolithic RBC bulk material, and SiC/graphite composite. The SiC/RBC composites not only had superior fracture strength (3-4 times as high as that of the monolithic RBC material) but also showed low friction coefficients (around 0.25) and high wear resistance (at a level of 10-6 mm3 N-1 m-1) when slid against a silicon carbide ceramic counterface during block-on-ring sliding tests under dry conditions. Compared with the conventional SiC/ graphite composite, the SiC/RBC composites had higher mechanical strength, lower friction coefficients, and better wear resistance.

Original languageEnglish
Pages (from-to)3439-3448
Number of pages10
JournalJournal of Materials Research
Volume20
Issue number12
DOIs
Publication statusPublished - 2005 Dec 1

ASJC Scopus subject areas

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering

Fingerprint Dive into the research topics of 'Preparation and tribological properties of SiC/rice bran carbon composite ceramics'. Together they form a unique fingerprint.

Cite this