Preparation and protium absorbing properties of Mg-based ternary alloys

H. Takarnura, T. Amemiya, Atsunori Kamegawa, M. Okada

Research output: Contribution to journalConference articlepeer-review

4 Citations (Scopus)

Abstract

The protium absorbing properties of Mg-Y-Ni, Mg-Y-Cu, and Mg-Al-Cu ternary alloys have been investigated in conjunction with phases present and microstructures. The alloys with a Mg-rich composition (≈80 at%Mg) were prepared by a flux-melting technique. It was found that the Mg-10Y-10Ni alloy with Mg, Mg24Y5, Mg2Ni, and MgNi2 (C15-type Laves structure) phases formed hydrides of Mg2Ni and Mg at 373 and 473 K, respectively. The decrease in the reaction temperature can be attributed to a morphological improvement, where Mg and Mg24 Y5 main phases with a needle-like shape surrounded by the Mg2Ni and MgNi2 phases, and/or the effect of Y incorporated into these phases. The Mg-10Y-10Ni alloy absorbed 4.O and 4.5 mass% of protium at 473 and 573 K, respectively. For the Mg-10Y-10Cu alloy, a two-step plateau regime was observed due to the disproportionation of the Mg2Cu phase. The Mg-6Y-24Cu alloys exhibited a protium storage capacity of 3.4 mass%, and its plateau pressure for the desorption process was about 0.08 MPa at 523 K. The Mg-10Al-10Cu alloy absorbed 4.5 mass% of protium. However, a temperature as high as 573 K was needed for observing the protium absorption -desorption process.

Original languageEnglish
Pages (from-to)315-320
Number of pages6
JournalMaterials Science Forum
Volume350
Publication statusPublished - 2000 Jan 1
EventProceedings of the 1st Nagaoka International Workshop on Magnesium Platform Science and Technology 2000 - Nagaoka, Jpn
Duration: 2000 Jul 272000 Jul 29

ASJC Scopus subject areas

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering

Fingerprint Dive into the research topics of 'Preparation and protium absorbing properties of Mg-based ternary alloys'. Together they form a unique fingerprint.

Cite this