Preparation and properties of ferromagnetic FePt dispersion

K. Sato, B. Jeyadevan, K. Tohji

Research output: Contribution to journalArticlepeer-review

22 Citations (Scopus)

Abstract

FePt nanoparticles were prepared via the coreduction of platinum and iron acetyl acetonate precursors in tetraethylene glycol at various temperatures. The X-ray diffractogram of the as-synthesized FePt nanoparticles at temperatures above 573 K exhibited (0 0 1) and (1 1 0) superlattice reflections. TEM-EDX studies revealed that the average particle diameter was 5 nm with nearly equiatomic composition. The saturation magnetization and coercivity at room temperature (RT) were found to be 50 emu/g and 2.1 kOe, respectively. The high anisotropy field of about 32 kOe and magnetic ordering at RT revealed the presence of the highly anisotropic L10 phase. These particles were partially dispersed in an organic solvent using oleyl amine as surfactant. The dispersed FePt nanoparticles will be useful in future technological applications.

Original languageEnglish
Pages (from-to)1-4
Number of pages4
JournalJournal of Magnetism and Magnetic Materials
Volume289
DOIs
Publication statusPublished - 2005 Mar

Keywords

  • Dispersed FePt
  • FePt
  • FePt magnetic fluids
  • FePt nanoparticles
  • High coercivity

ASJC Scopus subject areas

  • Electronic, Optical and Magnetic Materials
  • Condensed Matter Physics

Fingerprint Dive into the research topics of 'Preparation and properties of ferromagnetic FePt dispersion'. Together they form a unique fingerprint.

Cite this