Preliminary study on (CoPtCr/NiFe)-SiO2 hard/soft-stacked perpendicular recording media

Y. Inaba, T. Shimatsu, O. Kitakami, H. Sato, T. Oikawa, H. Muraoka, H. Aoi, Y. Nakamura

Research output: Contribution to journalArticlepeer-review

26 Citations (Scopus)

Abstract

Hard/soft-stacked perpendicular recording media were proposed in order to improve recording writability without notable changes in thermal stability and noise performance. A preliminary study on stacked media consisting of a 10-nm magnetically hard CoPtCr-SiO2 layer underneath a soft NiFe-SiO 2 layer (0-4 nm) was performed. Transmission electron microscope images revealed that NiFe/CoPtCr stacked grains were well isolated by SiO 2 at grain boundaries, similar to the isolation of single layer CoPtCr-SiO2 media. No change was observed in the slope of the hysteresis loop on stacking the NiFe-SiO2 layer, suggesting there was no significant change in intergranular magnetic coupling. The switching field decreased by 2 kOe as the NiFe-SiO2 layer thickness increased from 0 to 3 nm, without a notable reduction in the stabilizing thermal energy barrier. Moreover, the angular dependence of remanence coercivity indicates that magnetization reversal occurs by coherent rotation in (CoPtCr/NiFe)-SiO 2 stacked media as predicted theoretically, and no significant difference in switching mechanism from single layer CoPtCr-SiO2 media was observed. We successfully demonstrated that the hard/soft-stacked media show a better recording writability with no notable change in signal-to-media-noise ratio or thermal stability.

Original languageEnglish
Pages (from-to)3136-3138
Number of pages3
JournalIEEE Transactions on Magnetics
Volume41
Issue number10
DOIs
Publication statusPublished - 2005 Oct

Keywords

  • CoPtCr-SiO
  • Coercivity
  • Hard/soft-stacked media
  • Media noise
  • NiFe-SiO
  • Perpendicular recording media
  • Thermal stability

ASJC Scopus subject areas

  • Electronic, Optical and Magnetic Materials
  • Electrical and Electronic Engineering

Fingerprint Dive into the research topics of 'Preliminary study on (CoPtCr/NiFe)-SiO<sub>2</sub> hard/soft-stacked perpendicular recording media'. Together they form a unique fingerprint.

Cite this