Precipitation behavior and properties of Cu-Ti alloys with added nitrogen

Jun Ikeda, Satoshi Semboshi, Akihiro Iwase, Weilin Gao, Akira Sugawara

Research output: Contribution to journalArticle

2 Citations (Scopus)

Abstract

The effects of adding nitrogen (N) to age-hardenable Cu-Ti alloys on their microstructure, hardness, and conductivity have been investigated. It was found that the aging of Cu-Ti-(0.060.6) mol% N alloys resulted in the continuous formation of finely precipitated needleshaped α-Cu4Ti grains and the discontinuous formation of coarse cellular components composed of a stable β-Cu4Ti and Cu solid solution at the grain boundaries, in a manner similar to that in the case of conventional Cu-Ti alloys without any N. Furthermore, a small amount of granular TiN particles was also formed in Cu-Ti-N alloys. The hardening behavior of Cu-Ti-N alloys was similar to that of Cu-Ti alloys without N. This similarity was attributed to the finely dispersed precipitation of α-Cu4Ti that was similar between Cu-Ti alloys with and without N. The electrical conductivity of Cu-Ti-N alloys increased more steeply than that of Cu-Ti alloys without N. This is because in the case of Cu-Ti-N alloys, the coprecipitation of α-Cu4Ti, β-Cu4Ti, and TiN efficiently reduced the Ti concentration in the matrix. Thus, the conductivity of peak-hardened Cu-Ti- N alloys can be improved by optimizing the N concentration and aging temperature.

Original languageEnglish
Pages (from-to)297-302
Number of pages6
JournalMaterials Transactions
Volume56
Issue number3
DOIs
Publication statusPublished - 2015

Keywords

  • Aging
  • Copper-titanium alloy
  • Electrical conductivity
  • Hardness
  • Nitrogen
  • Precipitate

ASJC Scopus subject areas

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering

Fingerprint Dive into the research topics of 'Precipitation behavior and properties of Cu-Ti alloys with added nitrogen'. Together they form a unique fingerprint.

  • Cite this