PHASE RELATIONSHIP AND DENITRIFICATION DURING THE SINTERING PROCESS OF TiN-Ni MIXED POWDER COMPACTS.

Mikio Fukuhara, Hiroyasu Mitani

Research output: Contribution to journalArticlepeer-review

11 Citations (Scopus)

Abstract

The nickel-rich portion of the vertical section between nickel-solid solution and titanium nitride was studied using both sintered and arc-melted alloy specimens where a quasi-binary eutectic was found. The eutectic composition was about 10 wt% Ti and 1. 6wt% N, and the melting point was 1626 plus or minus 4K. Nitrogen gas was liberated upon formation of nickel-solid solution, but not from the liquid phase during sintering.

Original languageEnglish
Pages (from-to)211-218
Number of pages8
JournalTransactions of the Japan Institute of Metals
Volume21
Issue number4
DOIs
Publication statusPublished - 1980 Jan 1

ASJC Scopus subject areas

  • Engineering(all)

Fingerprint Dive into the research topics of 'PHASE RELATIONSHIP AND DENITRIFICATION DURING THE SINTERING PROCESS OF TiN-Ni MIXED POWDER COMPACTS.'. Together they form a unique fingerprint.

Cite this